Anti-alkali fabrics can be used as filter mesh in high temperature, the material with alkali content(sodium hydroxide) ≥ 20%. And it's also used in some industry that need high tensile strength and high wear resistance. Widely used in environmental protection,paper,industry waster water treatment,etc. Especially can be used in 100ºC,alkali content ≤20%. With functions such as High alkali resistance, corrosion resistance, wear resistance, high durability and best tensility, long life service, stable physical property against heat, etc.
Technical Parameter:
Code | Material | Wire Diameter | Density | Strength | Weight | Thickness | Air permeability | CFM 127/Pa | |||
mm | root/cm | N/cm | kg/m² | mm | (m³/m²h) | ||||||
warp | weft | warp | weft | surface | joint | ||||||
121104 | Pa6 | 0.9 | 1.1 | 12.8 | 4 | 1600 | 900 | 1.57 | 3.05 | 9600 | 600 |
15905 | Pa6 | 0.9 | 0.9 | 15.3 | 5 | 1600 | 900 | 2 | 2.77 | 6800 | 425 |
61204 | Pa6 | 1.2 | 1.2 | 7 | 4.3 | 1600 | 900 | 1.9 | 2.9 | 6895 | 431 |
81204 | Pa6 | 1.05 | 1.2 | 8.6 | 4.3 | 1600 | 900 | 2 | 2.9 | 6200 | 387 |
121204 | Pa6 | 1.05 | 1.2 | 12.6 | 4.1 | 1600 | 900 | 2.08 | 3.5 | 12050 | 659 |
16903 | Pa6 | 0.7 | 0.9 | 16.3 | 5 | 1600 | 900 | 1.5 | 2.1 | 7520 | 470 |
Product Description：
Anti-alkali fabrics can be used as filter mesh in high temperature, the material with alkali content(sodium hydroxide) ≥ 20%. And it's also used in some industry that need high tensile strength and high wear resistance. Widely used in environmental protection,paper,industry waster water treatment,etc. Especially can be used in 100ºC,alkali content ≤20%. With functions such as High alkali resistance, corrosion resistance, wear resistance, high durability and best tensility, long life service, stable physical property against heat, etc.
Technical Parameter:
Code | Material | Wire Diameter | Density | Strength | Weight | Thickness | Air permeability | CFM 127/Pa | |||
mm | root/cm | N/cm | kg/m² | mm | (m³/m²h) | ||||||
warp | weft | warp | weft | surface | joint | ||||||
121104 | Pa6 | 0.9 | 1.1 | 12.8 | 4 | 1600 | 900 | 1.57 | 3.05 | 9600 | 600 |
15905 | Pa6 | 0.9 | 0.9 | 15.3 | 5 | 1600 | 900 | 2 | 2.77 | 6800 | 425 |
61204 | Pa6 | 1.2 | 1.2 | 7 | 4.3 | 1600 | 900 | 1.9 | 2.9 | 6895 | 431 |
81204 | Pa6 | 1.05 | 1.2 | 8.6 | 4.3 | 1600 | 900 | 2 | 2.9 | 6200 | 387 |
121204 | Pa6 | 1.05 | 1.2 | 12.6 | 4.1 | 1600 | 900 | 2.08 | 3.5 | 12050 | 659 |
16903 | Pa6 | 0.7 | 0.9 | 16.3 | 5 | 1600 | 900 | 1.5 | 2.1 | 7520 | 470 |